Product introduction

5245 is atwo-component aliphaticisocyanate-cured acrylicpolyurethane topcoat. it has a high solid content and excellentweather resistance. its paint film is tough with high mechanicastrength and good chemical resistance.

Recommended applications

This product can be used as a topcoat for moderate to severeatmospheric corrosion environment requiring weather resistanceperformance,such as gloss and color retention.

Product information

Appearance：Adjustable color, half light

Volume solids：65±2%

Proportion：10 :1 (volume ratio)or 13.2 :1(weight ratio)

Recommended DFT：60 μm (corresponding WFT=92 μm)

Theoretical quantity required (60 μm)：10.8 m² /L or 7.45 m² /L

SG：1.45 kg/L

Flash point：Above 29℃

VOCs：352 g/L

Mixture's pot life (20°c after mixing)：2.5h

Full cure (20℃)：7d

Construction conditions

The substrate should be clean and dry. The paintingtemperature should be higher than 3'C above the dew pointto avoid condensation.

Curing agent is sensitive to moisture, so it is recommended to apply this product at<85%RH.

This product can be applied at temperature lower to -10℃.

Adequate ventilation is required during drying.

Painting method

Painting methods：airless spraying/air spraying/brush coating/roller coating

Diluent：109 epoxy diluent

Dilution：0-5% of the coating weight, The actual addition may be adjusted according to the field painting method

Nozzle size：0.43-0.48 mm

Spraying pressure：14 Mpa

Packing specifications：Component A:24kg,component B:1.8kgor Component A:16L, Component B: 1.6L

Shelf life：24 months for base material , 24 months for curing agent

Detergent：109 Diluent (after painting, clean the equipment in timeto avoid paint curing)

Safety measures：Refer to our Material Safety Data Sheet(MSDs)

Disclaimer: The above produtiformatin and data are accumulated acordina to ou experience in experiments and pracicaluse, and can be used as a constuction quideFor painting works that we are not informed, we ony guarantee the qualty ofthe coating itsel,butwe are not responsilble for other problems. We have the righto modify thimanualdue to the continuous improvement of our product.